Pengaruh Arus Pengelasan Terhadap Kekerasan Hasil LasPelat Baja Karbon S45c  Dengan Proses SMAW

Tulus Swasono; Emon Azriadi

doi:10.59061/jsit.v1i2.119

Authors

Tulus Swasono
Emon Azriadi

DOI:

https://doi.org/10.59061/jsit.v1i2.119

Abstract

Welding is a process of joining two or more metals which is widely applied in the industrial world. To get good welding results, it is necessary to choose the right amount of current. In this study, variations in the amount of current used were 60 A, 70 A and 80 A for welding S45C carbon steel plates, using the SMAW welding method. The results of the welding were then tested for hardness using the Rockwell HRB scale method in the weld metal, HAZ, and base metal areas. From the results of this study, the hardness value in the weld metal area was higher than the hardness value in the HAZ and base metal areas. And a good current used in welding S45C carbon steel plates is a welding current of 80 A.

References

Karohika, I Made Gatot. 2009. Pengaruh Variasi Arus dan Jenis Elektrode Pada Pengelasan SMAW Terhadap Sifat Mekanik Baja Karbon. Kampus Bukit Jimbaran Badung.

Kurniawan, Didit. 2010. Pengaruh Jenis Elektroda Pada Pengelasan Dengan Smaw Terhadap Sifat Fisis dan Mekanis Pada Baja Profil IWF. Universitas Muhammadiyah Surakarta.

Asfarizal. 2008. Pengaruh Masukan Panas Pengelasan Kampuh V Terhadap Struktur Mikro. Institut Teknologi Padang.

Asngari, Agung Hari. 2008. Pengaruh Arus Listrik Terhadap Daerah HAZ Las Pada Baja Karbon. Surakarta.

Akuan, Abrianto. 2009. Teknik Pengelasan Logam. Fakultas Teknik Universitas Jenderal Achmad Yani. Bandung.

Cary, Howard B. 1998, Modern Welding Technology. 4nd edition, Prentice Hall, New Jersey.

Daryus, Asyari. 2008. Proses Pengelasan dan Cacat Las Yang Terjadi. Jakarta.

Djamiko, Riswan Dwi. 2008. Modul Pengelasan Logam. Fakultas Teknik Universitas Negeri Yogyakarta.

Haryadi, Gunawan. 2007. Analisa Kerusakan Hasil Pengelasan Bawah Air Pada Lambung Kapal Dengan Bahan Elektroda Rb 26 Terseloti. Fakultas teknik mesin FT-UNDIP.

International Welding Inspection Personnel. Kemetrian Perindustrian RI Balai Besar Bahan dan Barang Teknik. Bandung.

Winarto. 2008. Desain Las. Fakultas Teknik Universitas Indonesia.

Wiryosumarto, Harsono, 2000. Teknologi Pengelasan Logam, Erlangga, Jakarta.

Wiryosumarto, Harsono. Toshie, Okumura. 1994. Teknologi Pengelasan Logam, PT. Pradnya Paramitha. Jakarta.

Wiryosumarto, Harsono. Toshie, Okumura. 2004. Teknologi Pengelasan Logam. Cetakan ke-9, Penerbit Pradnya Paramitha. Jakarta.

International Welding Inspection Personnel. Kemetrian Perindustrian RI Balai Besar Bahan dan Barang Teknik. Bandung.

Manual Book, Hardness Test Rockwell.

Santhiarsa, I Gusti Ngurah Nitya dan Budiarsa, I Nyoman. 2008. Pengaruh Posisi Pengelasan dan Gerakan Elektroda Terhadap Kekerasan Hasil Las Baja JIS SSC 41. Bali.

Salmon, Dkk. 1991. Struktur Baja, Disain dan Perilaku, jilid 1 dan 2, Edisi kedua.Santoso, Joko. 2006. Pengaruh Arus Pengelasan Terhadap Kekuatan Tarik dan Ketangguhan Las Smaw Dengan Elektroda E7018. Universitas Negeri Semarang.