Pengaruh Media Pendingin PKO Terhadap Kekuatan Tarik Hasil Pengelasan SMAW Pada Baja S45C

Authors

  • Indah Purnama Putri Politeknik Kampar
  • Adi Febrianton Politeknik Kampar

DOI:

https://doi.org/10.59061/repit.v1i4.477

Keywords:

SMAW Welding, PKO, Cooling Media, Medium Carbon Steel, Tensile Test

Abstract

The use and utilization of steel in the industrial world is very extensive because steel has unique properties, especially its strength. All tooling equipment cannot be separated from the engineering process and repair in the event of damage, namely by welding. One of the things that must be considered in welding is the cooling process. The purpose of the research was conducted to determine the effect of the cooling process on welding on the tensile strength of medium carbon steel using palm waste as a cooling medium. Tensile test samples were made with 3 variations of cooling media (PKO 100%, PKO75%, PKO 50%) using a HUNG TA HT-8503 machine. The highest tensile strength value was obtained from the 75% PKO variation with a tensile strength value of 345.58 Mpa. While the lowest tensile strength value is obtained from the 50% PKO variation with a tensile strength value of 232.28 Mpa.

References

Bintoro, G.A., 2000. Dasar-dasar Pekerjaan Las. Yogyakarta: Kansius. Cetakan ke-9, penerbit Pradnya Paramitha. Jakarta.

Daryanto., 2012. Teknik Las. Bandung: Alfabeta.

Joko Santoso, 2006. Pengaruh Arus Pengelasan Terhadap Kekuatan Tarik Dan Ketangguhan Las Smaw Dengan Elektroda E7018. Fakultas Teknik

Murhadi. 2010. The emultion stability of coconut (Cocos nucifera l.) milk added with ethanolysis product from palm kernel oil(Elaeis queneensis Jack). Proceeding International Seminar on Horticulture to Support Food Security 2010 June 22-23, 2010. Bandar Lampung. Hal. B-223-B229

Rifki ,L. 2017. Analisis Pengaruh Media Pendingin Dan Temperatur Pada Proses Pengerasan Baja Karbon Sedang Terhadap Sifat Kekerasan Dan Struktur Mikro Untuk Aplikasi Hammer Crusher. Institut Teknologi Sepuluh Nopember Surabaya.

Surdia, T. & Saito, S., 1999. Pengetahuan Bahan Teknik. Cetakan ke 4, Jakarta: PT Pradya Paramita.

V. Debora Saragih, K. Mea. Melaca, R. Darmawan, N. Hendrianie Departemen Teknik Kimia, Fakultas Teknologi Industri, Institut Teknologi Sepuluh Nopember (ITS)., 2018. Pra Desain Pabrik CPO (Crude Palm Oil) dan PKO (Palm Kernel Oil) Dari Buah Kelapa Sawit. Jurnal Teknik.

Widharto, S., 2001. Petunjuk Kerja Las. Jakarta: PT Pradya Paramita.

Wiryosumarto, Harsono. Thosie, Okumura.2000. Teknologi Pengelasan Logam.

Wiryosumarto. H, Okumura. T, Teknologi Pengelasan Logam, Pt. Pradnya Paramitha, Jakarta Cetakan ke 8. 2000

Downloads

Published

2023-11-27

How to Cite

Indah Purnama Putri, & Adi Febrianton. (2023). Pengaruh Media Pendingin PKO Terhadap Kekuatan Tarik Hasil Pengelasan SMAW Pada Baja S45C. Jurnal Rekayasa Proses Dan Industri Terapan, 1(4), 12–22. https://doi.org/10.59061/repit.v1i4.477

Similar Articles

<< < 1 2 

You may also start an advanced similarity search for this article.